Abstract:Experiments are conducted to study the effects of the forming process on the properties of high strength packaging materials made from waste corrugated containers. The results are as follows. With the same degree of beating, increase of the hotpressing pressure can improve the tensile strength, elongation at break, and modulus of elasticity; Increase of the hot- pressing temperature can only improve the tensile strength and modulus of elasticity. When the hot-pressing temperature is 165℃, beating degree is 35°SR and hot pressing pressure is 2 MPa, the elongation at break is the largest. And the peak of burst degree appears at the condition of 150℃, 27°SR, and 5 MPa. The higher the hot press temperature, the smaller the pressure and, the better the stiffness. The results also show that in order to save energy and shorten the preparation cycle, a better molding process scheme uses 27°SR beating degree and 165℃ hot-pressing temperature, while 5 MPa hot pressing drying or 0.08 MPa vacuum drying condition can be selected according to the specific demand.
李琛, 荣人慧, 肖生苓. 成型工艺对废旧瓦楞纸箱制备包装材料性能的影响[J]. 科技导报, 2015, 33(12): 61-66.
LI Chen, RONG Renhui, XIAO Shengling. Influence of molding process on the properties of packaging materials made from waste corrugated containers. Science & Technology Review, 2015, 33(12): 61-66.
[1] 胡英华. 废纸纤维包装材料加工工艺研究[D]. 天津: 天津科技大学, 2010. Hu Yinghua. Study on process and properties of wastepaper based packaging materials[D]. Tianjin: Tianjin University of Science & Technology, 2010.
[2] 张春红. 我国废纸的回收利用现状及发展趋势[J]. 西部纸业论坛, 2006, 2(35): 7-8. Zhang Chunhong. Waste paper recycling situation and development trend of our country[J]. Westesn Papermaking Industry Forum, 2006, 2 (35): 7-8.
[3] 姚培培, 肖生苓, 岳金全. 木质剩余物制备模塑包装材料研究进展[J]. 森林工程, 2014, 30(1): 96-99. Yao Peipei, Xiao Shengling, Yue Jinquan. Research progress on the preparation of molded packing material by wood residues[J]. Forest Engineering, 2014, 30(1): 96-99.
[4] 陈艳娜, 肖生苓, 李琛. 可降解木塑复合缓冲包装衬垫材料的研究综 述[J]. 森林工程, 2014, 30(2): 88-91. Chen Yanna, Xiao Shengling, Li Chen. Review on biodegradable foamed wood polymer composite buffering cushion packaging materials [J]. Forest Engineering, 2014, 30(2): 88-91.
[5] 高献策, 肖生苓, 曹斌, 等. 药用植物剩余物制作发泡包装材料工艺 及影响因素的分析[J]. 森林工程, 2012, 28(4): 65-68. Gao Xiance, Xiao Shengling, Cao Bin, et al. Analysis on the fabrication process and influencing factors of foaming packaging materials made by medicinal plant residues[J]. Forest Engineering, 2012, 28(4): 65-68.
[6] 戴宏民, 杨祖彬. 全降解植物纤维模塑餐具研发工作的进展[J]. 重庆 工商大学学报: 自然科学版, 2004(3): 221-222. Dai Hongmin, Yang Zubin. Progress in researches into plant fiber tableware[J]. Journal of Chongqing Technology and Business University: Natural Science Edition, 2004(3): 221-222.
[7] 丁毅, 李尧, 曾珊琪, 等. 植物纤维类缓冲包装材料的研制[J]. 包装工 程, 2006, 27(2): 50-51. Ding Yi, Li Yao, Zeng Shanqi, et al. Development of plant fiber cushion packaging material[J]. Packaging Engineering, 2006, 27(2): 50-51.
[8] 刘银鑫, 肖生苓, 岳金权, 等. 木质基包装材料在果蔬保鲜中的应用 [J]. 森林工程, 2014, 30(3): 140-142. Liu Yinxin, Xiao Shengling, Yue Jinquan, et al. The application of wood packing materials in the storage of fruits and vegetables[J]. Forest Engineering, 2014, 30(3): 140-142.
[9] 姚培培, 肖生苓, 岳金权. 利用木质剩余物与废纸制备纸浆模塑材料 的比较[J]. 森林工程, 2014, 30(4): 82-85. Yao Peipei, Xiao Shengling, Yue jinquan. Comparison of pulp molding material prepared by using wood residues and waste paper[J]. Forest Engineering, 2014, 30(4): 82-85.
[10] 朱秀刚. 一种植物纤维制品的生产方法: 中国, CN101579897[P]. 2009-11-18. Zhu Xiugang. A method for producing plant fibre products: China, CN101579897[P]. 2009-11-18.
[11] Shibata S, Cao Y, Fukumoto I. Press forming of short natural fiberreinforced biodegradable resin: Effects of fiber volume and length on flexural properties[J]. Polymer Testing, 2005, 24(8): 1005-1011.
[12] Byoung-Uk Cho, Jeong-Yong Ryu, Bong-Keun Song. Factors influencing deflaking kinetics in repulping to produce molded pulp[J]. Journal of Industrial and Engineering Chemistry, 2009, 15(1): 119- 123.
[13] Thumm A, Dickson A. The influence of fibre length and damage on the mechanical performance of polypropylene/wood pulp composites [J]. Composites Part A: Applied Science and Manufacturing, 2012.
[14] 姚培培, 肖生苓, 岳金权. 不同干燥方式对纸浆模塑材料性能的影响 [J]. 包装工程, 2014, 35(7): 22-28. Yao Peipei, Xiao Shengling, Yue Jinquan. Effects of different drying methods on the properties of molded pulp material[J]. Packaging Engineering, 2014, 35(7): 22-28.
[15] 王孟效, 孙瑜, 汤伟, 等. 制浆造纸过程测控系统及工程[M]. 北京: 化学工业出版社, 2003. Wang Mengxiao, Sun Yu, Tang Wei, et al. Pulping and papermaking process measurement and control system and engineering[M]. Beijing: Chemical Industry Press, 2003.
[16] 陈佩蓉, 屈维均, 何福望. 制浆造纸实验[M]. 北京: 轻工业出版社, 1990. Chen Peirong, Qu Weijun, He Fuwang. The experiment of pulping and papermaking[M]. Beijing: Chemical Industry Press, 1990.
[17] 任怀燕, 赵传山. 改进纸和纸板挺度的助剂[J]. 造纸化学品, 2008, 20(2): 29-31. Ren Huaiyan, Zhao Chuanshan. Stiffness additives of paper and paperboard[J]. Paper Chemicals, 2008, 20(2): 29-31.