Localized Electrochemical Impedance Spectroscopy of the Corrosion Behavior of Carbon Steel in the Alkaline Solutions with Cl- and SO42- |
WEI Dan1,2, XIAO Kui3, CHEN Changfeng1, LI Xiaogang3 |
1. Department of Materials Science and Engineering, China University of Petroleum, Beijing 102249, China;2. Service Center for Societies, China Association for Science and Technology, Beijing 100081, China;3. Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract: The corrosion behavior of carbon steel in the neutral and alkaline solutions with Cl- and SO42- were investigated by Localized Electrochemical Impedance Spectroscopy (LEIS) technique. The corrosion products on the surface of sample were analyzed by Laser Micro-Raman Spectrometry. The experimental results indicated that the corrosion rate in the neutral solution was higher than that in the alkaline solution during the initial stage of immersion. In the neutral solution, the corrosion products were rapidly deposited on the surface of the sample. The corrosion products film was composed of γ-FeOOH, which could protect matrix of Q235 carbon steel and reduce the ion penetration. As the immersion time increased, the Cl- and SO42- ions damaged corrosion product films. Especially in the alkaline solution during the initial stage, the average impedance value was much higher. But the average impedance rapidly decreased with increase of the steeping time. Moreover, the destructive effect of Cl- and SO42- ions on the passive film is also demonstrated in corrosion process through the change of impedance value as the steeping time increases.
|
Received: 28 April 2013
|
|
|
|
|
[1] |
ZHANG Zhihong, ZHANG Jiangjiang, GAO Qiuying, SUN Haijiao, XIAO Wenwen. Analysis of Rupture Failure of Sidetrack Deep Well Pipe in Tahe Oilfield[J]. journal1, 2014, 32(7): 62-66. |
[2] |
ZHANG Jiangjiang, LIU Jining, GAO Qiuying, YANG Dongming, ZANG Hanyu, ZHANG Tao, XIAO Wenwen, JIANG Rui. Sediment in the Formation in Wet CO2 Environment of Pipeline and Quantitative Study of Its Corrosion Effect[J]. Science & Technology Review, 2014, 32(32): 67-71. |
[3] |
ZHANG Jiangjiang. Tahe Oilfield Gas Pipeline Corrosion Characteristics and Rules[J]. Science & Technology Review, 2014, 32(31): 65-70. |
[4] |
LI Xiaobo, ZHANG Hailong. Erosion and Corrosion Superposition Mechanism of Thermal Screen[J]. journal1, 2014, 32(3): 49-55. |
[5] |
GUO Lin, XU Xiuqing. Influence of S2-Concentration on the Corrosion Resistance of 10# Carbon Steel in Saline Wastewater[J]. journal1, 2014, 32(24): 31-34. |
[6] |
GAO Qiuying, ZHANG Jiangjiang, YANG Zuguo, YANG Dongming, LIU Jining, ZANG Hanyu, ZHU Yuanyuan, ZHANG Tao. Effects of Sediments on the Corrosion Behavior of 20# Carbon Steel Pipe[J]. journal1, 2014, 32(24): 35-39. |
|
|
|
|