Corrosion Behavior and Law of Copper-Clad Laminate with Immersion Silver Layer in Salt Spray Environment |
XIAO Kui, ZOU Shiwen, DONG Chaofang, WU Junsheng, LI Xiaogang |
Corrosion and Protetion Center, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract: The corrosion behavior of Copper-Clad Laminate(CCL) with immersion silver layers in the neutral salt spray environment is studied by Electrochemical Impedance Spectroscopy(EIS). The surface morphology and the composition of corrosion products were analyzed by the SEM/EDS surface analysis methods. The results indicate that the immersion silver layers can protect the products in the salt spray environment. On the sample surface, no obvious corrosion could be seen in the initial stage and large impedance values were measured. But local damages would occur in the immersion silver layers due to the chlorides on the sample surface. The impedance values decrease with the test time. For a long salt spray test time, the immersion silver layers cannot effectively prevent corrosion reactions. The increase of the impedance values is due to the continued thickening of the copper rust layers, which prevent the incursion of harmful ions and the further corrosion of matrix.
|
Received: 17 June 2011
|
|
|
|
|
[1] |
GAO Qiuying, ZHANG Jiangjiang, YANG Zuguo, YANG Dongming, LIU Jining, ZANG Hanyu, ZHU Yuanyuan, ZHANG Tao. Effects of Sediments on the Corrosion Behavior of 20# Carbon Steel Pipe[J]. journal1, 2014, 32(24): 35-39. |
[2] |
LI Zifan, XIAO Kui, WEI Dan, DONG Chaofang, ZHANG Xin, LI Xiaogang. Corrosion Behavior of Fe-Cr Alloy in the Solution with Cl- and SO42-[J]. journal1, 2014, 32(21): 26-30. |
[3] |
ZOU Shiwen;XIAO Kui;DONG Chaofang;DING Kangkang;LI Xiaogang. Corrosion Behavior and Control Methods of Microbiologically Influenced Corrosion of Space Station Environmental Control and Life Support System[J]. , 2013, 31(30): 61-66. |
[4] |
SUN Min;XIAO Kui;DONG Chaofang;LI Xiaogang;ZHONG Ping. Stress Corrosion Cracking Behavior of Ultrahigh Strength Steel in the Atmospheric Environment[J]. , 2012, 30(30): 20-24. |
|
|
|
|