1. Research Institute of Material Forming and Control Engineering, Zhejiang University of Technology, Hangzhou 310014, China;
2. Research Institute of Chemical Machinery, Zhejiang University, Hangzhou 310027, China;
3. Mechanical and Electronic Engineering College, China University of Petroleum, Qingdao 266555, China
Abstract:In hydrogen energy, petroleum and chemical industries the bearing parts in high pressure hydrogen systems are prone to hydrogen-induced damage due to the coupling effect of manufacturing residual effects, high-pressure hydrogen and complicated loadings. In order to ensure long-term, stable, safe and reliable operations of the high-pressure hydrogen system, it is necessary to provide the data of material properties for the development of high-pressure hydrogen system products. Considering the independence and extendibility of data, a database for mechanical properties of metallic materials in high-pressure environment is developed with VB programming language. based on the materials data previously obtained in high-pressure hydrogen environments (slow strain rate tension test, fracture toughness test and fatigue crack propagation test). The analysis of the database, which combines domestic and foreign researches and applications, has shown its versatility and comprehensiveness in terms of metal material hydrogen embrittlement data.
[1] Eliezer D, Chakrapani D G, Altstetter C J, et al. The influence of austenite stability on the hydrogen embrittlement and stress-corrosion cracking of stainless steel[J]. Metallurgical Transoction A, 1979, 10(7): 935-941.
[2] Michler T, Naumann J. Hydrogen environment embrittlement of austenitic stainless steels at low temperatures[J]. International Journal of Hydrogen Energy, 2008, 33(8): 2111-2122.
[3] Martin M, Weber S, Theisen W, et al. Effect of alloying elements on hydrogen environment embrittlement of AISI type 304 austenitic stainless steel[J]. International Journal of Hydrogen Energy, 2011, 36(24): 15888-15898.
[4] Michler T, Marchi C S, Naumann J, et al. Hydrogen environment embrittlement of stable austenitic steels[J]. International Journal of Hydrogen Energy, 2012, 37(21): 16231-16246.
[5] Zhang L, Li Z Y, Zheng J Y, et al. Influence of low temperature prestrain on hydrogen gas embrittlement of metastable austenitic stainless steels[J]. International Journal of Hydrogen Energy, 2013, 38(25): 11181-11187.
[6] 南雲道彦. 钢的氢脆的新研究方向[J]. 热处理, 2010, 25(3): 1-6. Michihiko Nagumo. Turning of the research direction on hydrogen embrittlement of steels[J]. Heat Treatment, 2010, 25(3): 1-6.
[7] 李依依, 范存淦, 戎利建, 等. 抗氢脆奥氏体钢及抗氢铝[J]. 金属学报, 2010, 46(11): 1335-1346. Li Yiyi, Fan Cungan, Rong Lijian, et al. Hydrogen embrittlement resistance of austenitic alloys and aluminium alloys[J]. Acta Metallurgica Sinica, 2010, 46(11): 1335-1346.
[8] 陈瑞, 郑津洋, 徐平, 等. 金属材料常温高压氢脆研究进展[J]. 太阳能学报, 2008, 29(4): 502-508. Chen Rui, Zheng Jinyang, Xu Ping, et al. Hydrogen embrittlement of metallic materials in high-pressure hydrogen at normal temperature[J]. Acta Energiae Soleris Sinica, 2008, 29(4): 502-508.
[9] Shigeharu H, Fukunaga T, Takahashi K, et al. Hydrogen embrittlement of high strength steel in high pressure hydrogen at ambient temperature[J]. Journal of the Iron and Steel Institute of Japan, 1978, 64(7): 899-905.
[10] Wada Y, Ishigaki R, Tanaka Y, et al. Evaluation of metal materials for hydrogen fuel stations[A]. Proceedings of International Conference on Hydrogen Safety[C]. Pisa: ICHS, 2005.
[11] 周洪范, 张朝纲. 材料数据库的进展和应用[J]. 机械工程材料, 1993, 17(1): 1-4. Zhou Hongfan, Zhang Chaogang. The progress and application of materials database[J]. Materials for Mechanical Engineering, 1993, 17(1): 1-4.
[12] 史国川, 黄剑. Access 数据库技术与应用[M]. 北京:科学出版社, 2011: 1-337. Shi Guochuan, Huang Jian. Access database technology and application[M]. Beijing: Science Press, 2011: 1-337.
[13] 王红亮, 马志刚. Visual Basic 6.0程序设计[M]. 北京: 国防工业出版社, 2011: 1-324. Wang Hongliang, Ma Zhigang. Visual Basic 6.0 program design[M]. Beijing: National Defence Industry Press, 2011: 1-324.
[14] 田彬. SQL宝典[M]. 北京: 电子工业出版社, 2014: 1-500. Tian Bin. SQL bible[M]. Beijing: Publishing House of Electronics Industry, 2014: 1-500.
[15] Chandler W T, Walter R J. Hydrogen embrittlement testing[M]. Philadelphia: American Society for Testing and Materials, 1974:1-274.
[16] 赵林, 武建军. 灾害风险防范数据库的设计与开发[J]. 自然灾害学报, 2008, 17(1): 44-48. Zhao Lin, Wu Jianjun. Design and development of database for disaster risk governance[J]. J of Natural Disasters, 2008, 17(1): 44-48.
[17] 洋海棠, 杨瑞成, 袁晓波, 等. 耐磨料磨损材料数据库的设计与实现[J]. 材料科学与工艺, 2006,14(4): 345-348. Yang Haitang, Yang Ruicheng, Yuan Xiaobo, et al. Design and actualization of database of wear resistance materials[J]. Materials Science & Technology, 2006, 14(4): 345-348.
[18] 褚武扬, 乔利杰, 李金许, 等. 氢脆和应力腐蚀[M]. 北京: 科学出版社, 2013: 226-276. Chu Wuyang, Qiao Lijie, Li Jinxu, et al. Hydrogen embrittlement and stress corrosion cracking[M]. Beijing: Science Press, 2013: 226-276.
[19] Louthan M R, Caskey G R, Donovan J A, et al. Hydrogen embrittlement of metals[J]. Materials Science and Engineering, 1972, 10: 357-368.
[20] Capeletti T L, Louthan M R. The tensile ductility of austenitic steels in air and hydrogen[J]. Journal of Engineering and Technology, 1977, 99: 153-158.
[21] Marchi C S. Technical reference on hydrogen compatibility of materials-austenitic stainless steels: Type 316[M]. Sandia National Laboratories, 2005.
[22] Tamura M, Shibata K. Evaluation of mechanical properties of metals at 45 MPa hydrogen[J]. Journal of the Japan Institute of metals, 2005, 69(12): 1039-1048.
[23] Barthélémy H. Effects of pressure and purity on the hydrogen embrittlement of steels[J]. Hydrogen Energy, 2011, 36: 2750-2758.
[24] Mauro M, Wener T. Impact of the microstructure and surface finishing on the ductility response of AISI type 304L steel tested in high pressure hydrogen gas atmosphere[J]. Procedia Materials Science, 2015, 9: 396-403.
[25] Marchi C S, Michler T, Nibur K A, et al. On the physical differences between tensile testing of type 304 and 316 austenitic stainless steels with internal hydrogen and in external hydrogen[J]. Hydrogen Energy, 2010, 35: 9736-9745.