新型耐蚀低合金钢筋腐蚀行为

刘明; 程学群; 李晓刚; 邢佩; 洪媛媛; 魏子博

doi:10.3981/j.issn.1000-7857.2016.2.034

PDF(3979 KB)

科技导报 ›› 2016, Vol. 34 ›› Issue (2) : 205-209. DOI: 10.3981/j.issn.1000-7857.2016.2.034

综述文章

新型耐蚀低合金钢筋腐蚀行为

作者信息 -

北京科技大学腐蚀与防护中心, 北京 100083

作者简介:

刘明,博士研究生,研究方向为耐蚀钢筋的腐蚀机理与耐久性,电子信箱:liuming870313@stu.xjtu.edu.cn

Corrosion behavior of new low alloy corrosion resistance rebar

Author information -

Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China

摘要

应用动电位极化、电化学阻抗谱、周浸腐蚀试验的方法,研究了HRB400 碳钢钢筋和两种Cr 合金化的低合金钢筋在0.01mol/L NaHSO₃溶液中的腐蚀行为。结果表明,相比HRB400 钢筋,Cr 合金化钢筋的开路电位明显正移,Cr 元素提高了钢的热力学稳定性;随着Cr 元素质量分数的增加,钢筋的自腐蚀电流密度减小,极化电阻增大,Cr 合金化的钢筋具有相对较小的电化学腐蚀速率;周浸加速腐蚀72 h 后,HRB400 钢筋和Cr 合金化的钢筋均以均匀腐蚀为主,添加Cr 元素可以显著降低钢筋的均匀腐蚀速率。

Abstract

The electrochemical methods of the potentiodynamic polarization, the electrochemical impendence spectroscopy and the dry/wet cycle corrosion test are employed to investigate the corrosion behavior of the Cr modified HRB400 carbon steel rebar in 0.01 mol/L NaHSO₃ solution. The open circuit potential of the Cr modified steel shifts in the positive direction as compared with the HRB400 carbon steel; The results of the polarization curve show that the corrosion current density of the Cr modified steel is decreased, the polarization resistance is increased and the corrosion rate is declined. After the dry/wet cycle corrosion test for 72 h, the corrosion morphologies of the HRB400 steel and the Cr modified steel see a uniform corrosion, the addition of the Cr element can significantly reduce the corrosion rate of the HRB400 steel rebar.

导出引用

刘明, 程学群, 李晓刚, 邢佩, 洪媛媛, 魏子博. 新型耐蚀低合金钢筋腐蚀行为[J]. 科技导报, 2016, 34(2): 205-209 https://doi.org/10.3981/j.issn.1000-7857.2016.2.034

LIU Ming, CHENG Xuequn, LI Xiaogang, XING Pei, HONG Yuanyuan, WEI Zibo. Corrosion behavior of new low alloy corrosion resistance rebar[J]. Science & Technology Review, 2016, 34(2): 205-209 https://doi.org/10.3981/j.issn.1000-7857.2016.2.034

参考文献

[1] Du Y L, Shi Z M. The state of art on corrosion and prevention of reinforced concrete[J]. Journal of Jilin Institute of Technology, 1998, 19 (2): 2-12.
[2] 沈德建, 吴胜兴. 大气环境锈蚀钢筋混凝土梁力学性能试验研究及分析[J]. 土木工程学报, 2009, 42(8): 75-82. Sheng Dejian, Wu Shengxing. Experimental study and analysis on the mechanical performance of corroded reinforcement concrete beams in atmospheric environment[J]. China Civil Engineering Journal, 2009, 42 (8): 75-82.
[3] Mahdi V, Mohammad S, Pouria G. Comparative studies of experimental and numerical techniques in measurement of corrosion rate and timeto-corrosion-initiation of rebar in concrete in marine environments[J]. Cement and Concrete Composites, 2014, 48(1): 98-107.
[4] Criado M, Bastidas D M, Fajardo S, et al. Corrosion behaviour of a new low-nickel stainless steel embedded in activated fly ash mortars[J]. Cement and Concrete Composites, 2011, 33(6): 644-52.
[5] Luo H, Dong C F, Li X G, et al. The electrochemical behavior of 2205 duplex stainless steel in alkaline solutions with different pH in the presence of chloride[J]. Electrochimica Acta, 2012, 64(4): 211-220.
[6] 葛燕, 朱锡昶, 李岩. 桥梁钢筋混凝土结构防腐蚀——耐腐蚀钢筋及阴极保护[M]. 北京: 化学工业出版社, 2011. Ge Yan, Zhu Xiyong, Li Yan. Corrosion of reinforced concrete bridge structures[M]. Beijing: Chemical Industry Press, 2011.
[7] 郭湛, 完卫国, 孙维, 等. 含稀土高强度耐腐蚀钢筋的研究[J]. 钢铁, 2010, 42(12): 53-58. Guo Zhan, Wan Weiguo, Sun Wei, et al. Study on high strength and resisting corrosion steel bar containing Re[J]. Iron and Steel, 2010, 42 (12): 53-58.
[8] 周扬, 陈翠翠, 蔡景顺, 等. 耐蚀钢筋的腐蚀行为及其与阻锈剂的协同作用[J]. 建筑材料学报, 2015, 3(3): 16-27. Zhou Yang, Chen Cuicui, Cai Jingshun, et al. Corrosion behavior of corrosion resistant reinforcing steels and their synergistic effect with corrosion inhibitor[J]. Journal of Building Materials, 2015, 3(3): 16-27.
[9] Yamashita M, Miyuki H, Matsuda Y, et al. The long term growth of the protective rust layer formed on weathering steel by atmospheric corrosion during a quarter of a century[J]. Corrosion Science, 1994, 36 (2): 283-299.
[10] Hao L, Zhang S, Dong J, et al. Evolution of corrosion of MnCuP weathering steel submitted to wet/dry cyclic tests in a simulated coastal atmosphere[J]. Corrosion Science, 2012, 10(58): 175-180.
[11] Wang Z, Liu J, Wu L, et al. Study of the corrosion behavior of weathering steels in atmospheric environments[J]. Corrosion Science, 2013, 67(3): 1-10.
[12] Zhang P, Yu H. Microstructure and properties of seawater corrosion resistant steel 10CrMoAl[J]. Jouranl of Wuhan University Science Technology, 2010, 33(2): 176-179.
[13] Kamimura T, Stratmann M. The influence of chromium on the atmospheric corrosion of steel[J]. Corrosion Science, 2001, 43(3): 429-447.
[14] 中华人民共和国工业和信息化部. YB/T 4368-2014, 钢筋在工业大气环境中腐蚀试验方法[S]. 北京: 冶金工业出版社, 2014. Ministry of Industry and Information Technology of the People's Republic of China. YB/T 4368-2014, Corrosion test method for reinforcement in industrial atmospheric environment[S]. Beijing: Metallurgical Industry Press, 2014.
[15] Rocchini G. Evaluation of the electrochemical parameters by means of series expansion[J]. Corrosion Science, 1994, 36(8): 1347.
[16] 刘明, 薛玉娜, 高婷, 等. CT80连续油管钢在60℃高矿化水中的电化学腐蚀行为[J]. 腐蚀科学与防护技术, 2013, 25(3): 213-218. Liu Ming, Xue Yuna, Gao Ting, et al. Electrochemical corrosion behavior of a CT80 coiled tubing steel in 60℃ salinity solution[J]. Corrosion Science and Protetion Technology, 2013, 25(3): 213-218.
[17] Macdonald J R. Impedance spectroscopy[J]. Annals of Biomedical Engineering, 1992(20): 289-305.
[18] 伍远辉, 罗宿星, 付盈盈, 等. 氯离子环境下混凝土钢筋的电化学阻抗谱特征[J]. 表面技术, 2011, 40(3): 65-67. Wu Yuanhui, Luo Suxing, Fu Yingying, et al. Eis characteristics of the steel in concrete in environment containing chloride ion[J]. Surface Technology, 2011, 40(3): 65-67.
[19] Cheng X Q, Tian Y W, Li X G, et al. Corrosion behavior of nickel containing weathering steel in simulated marine atmospheric environment [J]. Materials and Corrosion, 2014, 8(65): 1033-1037.
[20] Zhao Y X, Ren H Y, Dai H, et al. Composition and expansion coefficient of rust based on X-ray diffraction and thermal analysis[J]. Corrosion Science, 2011, 53(5): 1646-1658.
[21] 邹妍, 王佳, 郑莹莹. 锈层下碳钢的腐蚀电化学行为特征[J]. 物理化学学报, 2010, 26(9): 2361-2368. Zou Yan, Wang Jia, Zheng Yingying, et al. Electrochemical corrosion behaviors of rusted carbon steel[J]. Journal of Physical Chemistry, 2010, 26(9): 2361-2368.