利用高温高压反应釜进行冲蚀、腐蚀和冲蚀腐蚀迭加3 种条件下的多元热流体稠油热采防砂筛管损坏模拟实验，采用失重法获得3 种条件下筛管挡砂介质的腐蚀速率，434 金属棉在迭加条件下的腐蚀速率较纯冲蚀条件下提高了75 倍，较纯腐蚀条件下也提高了53%。采用宏观观察、扫描电子显微镜（SEM）、能谱仪（EDS）等方法对腐蚀试样进行宏微观分析，发现迭加条件下材质腐蚀程度均比单一条件下显著。结果表明，在迭加作用下筛管材质的腐蚀速率显著高于单纯冲蚀和单纯腐蚀条件。腐蚀作用对机体的损伤以及冲蚀作用对腐蚀保护膜的破坏两方面相互促进，导致筛管材质损伤程度的增加。
Failure simulation experiments of multiple thermal fluid recovery sand control screen were firstly carried out in erosion, corrosion and erosion-corrosion superposition conditions. The experiments were carried out in high temperature and high pressure reaction still. The corrosion rates of screen block sand medium were respectively observed in three conditions by weight loss method, the corrosion rate of 434 material in superposition condition is 75 times higher than that in erosion condition and is 53% higher than that in corrosion condition. Macroscopic and microscopic analysis were carried out by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). Results showed that corrosion rates in superposition conditions were observably higher than those in single erosion and single corrosion conditions. The destructive effect of corrosion to organism and erosion to corrosion protective film promote mutually, which leads to the increase of damage degree.
[1] 马增华, 孙永涛, 林涛, 等. 多元热流体中不同钢材的腐蚀行为研究[J]. 石油化工应用, 2012, 31(9): 60-63. Ma Zenghua, Sun Yongtao, Lin Tao, et al. Study on corrosion behavior of different steels in multicomponent thermal fluid[J]. Petrochemical Indus-try Application, 2012, 31(9): 60-63.
[2] 王雪飞, 杨岐年, 赵启彬. 多元热流体吞吐技术在海洋稠油探井测试中 的应用[J]. 油气井测试, 2011, 20(3): 35-36. Wang Xuefei, Yang Qinian, Zhao Qibin. Application of multicomponent thermal fluid swallow and spit technology in heavy oil exploratory well testing[J]. Well Testing, 2011, 20(3): 35-36.
[3] 孙永涛, 付朝阳, 杨秀兰, 等. 高温多元热流体注采中管材腐蚀分析[J]. 石油与天然气化工, 2012, 41(4): 408-410. Sun Yongtao, Fu Chaoyang, Yang Xiulan, et al. Corrosion analysis of oil pipe in injection exploitation of high temperature multicomponent ther-mal fluid[J]. Chemical Engineering of Oil & Gas, 2012, 41(4): 408-410.
[4] 余焱冰. 多元热流体注热管柱腐蚀机理研究[J]. 化工管理, 2013, 5: 132. Yu Yanbing. Research on corrosion mechanism of multicomponent ther-mal fluid injection pipe[J]. Chemical Enterprise Management, 2013, 5: 132.
[5] Peter T, Declan L, Theosore H. New sand-control filter of thermal recov-ery wells[J]. SPE Production Engineering, 1988, 3(2): 249-257.
[6] 刘新锋, 张海龙, 李效波, 等. 海上稠油热采筛管冲蚀影响因素[J]. 石油 钻采工艺, 2012, 34(S1): 73-75. Liu Xinfeng, Zhang Hailong, Li Xiaobo, et al. Influence factors study on screen erosion of offshore heavu crude thermal extration[J]. Oil Drill-ing & Production Technology, 2012, 34(S1): 73-75.
[7] 刘永红, 张建桥, 马建民, 等. 石油防砂割缝筛管的冲蚀磨损性能研 究[J]. 摩擦学学报, 2009, 29(3): 283-287. Liu Yonghong, Zhang Jianqiao, Ma Jianmin, et al. Erosion wear behav-ior of slotted screen liner for sand control[J]. Tribology, 2009, 29(3): 283-287.
[8] 张安峰, 王豫跃, 邢建东. 不锈钢与碳钢在液固两相流中冲刷腐蚀特 性的研究[J]. 兵器材料学与工程, 2003, 26(2): 36-39. Zhang Anfeng, Wang Yuyue, Xing Jiandong. Erosion-corrosion charac-teristics of carbon steel and stainless steel in dual-phase fluids[J]. Ordnance material Science and Engineering, 2003, 26(2): 36-39.
[9] 贾恒磊, 赵春平, 汪浩, 等. 管线的氧浓差电池现象[J]. 管道技术与 设备, 2012(3): 51-52. Jia Henglei, Zhao Chunping, Wang Hao, et al. Phenomenon of oxygen concentration cell in pipeline[J]. Pipeline Technique and Equipment, 2012(3): 51-52.
[10] 戈仁刚. 海洋油井套管断裂原因分析[J]. 腐蚀研究, 2011, 25(7): 45-48. Ge Rengang. Failure analysis of marine casing[J]. Corrosion Research, 2011, 25(7): 45-48.
[11] 杨剑蓉. 热水加热器的失效分析[J]. 化工设计, 2007, 17(2): 35-37. Yang Jianrong. Failure analysis of heat-water heater[J]. Chemical Engi-neering Design, 2007, 17(2): 35-37.