为研究Fe-Cr 合金在含Cl-和SO42- 离子溶液中浸泡的腐蚀行为，采用显微激光拉曼光谱技术进行腐蚀产物分析，并进行线性极化和交流阻抗电化学测试明确腐蚀机理。研究结果表明，Fe-Cr 合金含有大量Cr 更容易形成钝化膜，在浸泡初期Fe-Cr 合金腐蚀速度很小。随着浸泡时间增加，维钝电流密度呈现先增加而后明显减小的趋势，说明钝化膜不断加强，钝化膜起到较好的阻碍Cl-和SO42- 阴离子侵蚀作用。在酸性溶液中，Fe-Cr 合金钝化的同时也发生着点蚀，且随着浸泡时间的增长而加剧。Fe-Cr合金在浸泡150 h 后，在三角晶界及其附近的晶界更易出现腐蚀产物，这是由于模拟溶液中含有大量Cl-离子，致使钝化膜破损。而在Fe-Cr 合金的腐蚀产物中出现CrOOH，对腐蚀有抑制作用。
The corrosion behaviors of Fe-Cr alloy in the acidic solutions with Cl- and SO42- are investigated. The corrosion mechanisms are characterized by the linear polarization and the electrochemical impedance spectroscopy measurements, and the corrosion products are analyzed by the laser Raman spectrometry. It is shown that the Fe-Cr alloy is attributed for the passive film, which is formed more easily when the alloy contains a large quantity of Cr element. In the early immersion, the corrosion rate of Fe-Cr alloy is very small. With the immersion time increases, the passive current density firstly increases, and then decreases. The passive film can well prevent the Cl- and SO42- anion erosions. For Fe-Cr alloy, pitting occurs in an acidic solution, and it increases its extent with the increase of the immersion time. If the Fe-Cr alloy is immersed in the solutions for 150 h, the corrosion products appear in the near grain boundary, and are more likely to occur in the triangle grain boundary. The corrosion products of the Fe-Cr alloy contain CrOOH.
[1] Revie R W. Uhlig's corrosion handbook[M]. 2nd ed. New York: John Wiley and Sons, 2000.
[2] Roberge P R. Handbook of corrosion engineering[M]. New York: McGraw-Hill, 2000.
[3] Shreir L L, Jarman R A, Burstein G T. Corrosion: vol 1 Metal/environment reactions[M]. 3rd ed. Oxford: Butterworth Heinemann, 1994.
[4] 王世伟, 李瑛, 王林山. 土壤中侵蚀性离子对X70钢的侵蚀作用研究[J]. 腐蚀科学与防护技术, 2005, 17(2): 98-100. Wang Shiwei, Li Ying, Wang Linshan. Effect of aggressive ions in soils on corrosion behavior of X70 steel[J]. Corrosion Science and Protection Technology, 2005, 17(2): 98-100.
[5] 刘文霞, 孙成. 土壤中阴离子对碳钢腐蚀的影响[J]. 石油化工腐蚀与防护, 2006, 23(5): 12-15. Liu Wenxiao, Sun Cheng. Effects of different cathodic ions on the corrosion of carbon steel in soils[J]. Corrosion & Protection in Petrochemical Industry, 2006, 23(5): 12-15.
[6] Atenas G M, Mielczarski E, Mielczarski J A. Composition and structure of iron oxidation surface layers produced in weak acidic solutions[J]. Journal of Colloid and Interface Science, 2005, 289(1): 157-170.
[7] Wang Z S, Xu C C, Dong X Q. Localized corrosion and phase transformation of simulated archaeological iron[J]. Chinese Journal of Chemical Engineering, 2008, 16(2): 299-305.
[8] Ismail A I M, El-Shamy A M. Engineering behaviour of soil materials on the corrosion of mild steel[J]. Applied Clay Science, 2009, 42(3-4): 356-362.
[9] Schweitzer P A. Corrosion engineering handbook—Fundamentals of metallic corrosion[M]. 2nd ed. New York: CRC Press, 2007.
[10] Gerwin W, Baumhauer R.Effect of soil parameters on the corrosion of archaeological metal finds[J]. Geoderma, 2000, 96(1): 63-80.
[11] Talbot D E J, Talbot J D R. Corrosion science and technolgy[M]. New York: CRC Press, 1998.
[12] Tang Y C, Katsuma S, Fujimoto S, et al. Electrochemical study of type 304 and 316L stainless steels in simulated body fluids and cell cultures[J]. Acta Biomaterialia, 2006, 2(6): 709-715.
[13] Zeng Y M, Luo J L. Electronic and structure of passive film on X70 pipeline steel[J]. Electrochimica Acta, 2003, 48(23): 3551-3562.
[14] Zeng Y M, Luo J L, Norton P R. Initiation and propagation of pitting and crevice corrosion of hydrogen-containing passive film on X70 micro-alloyed steel[J]. Electrochimica Acta, 2004, 49(5): 703-714.
[15] Maslar J E, Hurst W S, Bowers W J, Jr. In situ Raman spectroscopic investigation of chromium surfaces under hydrothermal conditions[J]. Applied Surface Science, 2001, 180(1-2): 102-118.