In the present work, the effects of quenching transfer time on the mechanical properties and microstructure of A357 aluminum alloys are investigated by using optical microscopy (OM), scanning electron microscope (SEM), differential scanning calorimetry (DSC), transmission electron microscopy (TEM), as well as tensile mechanical properties testing methods. The results show that with the increase of quenching transfer time from 3 s to 49 s, the tensile strength, yield strength and elongation of A357 aluminum alloys are reduced from 351 MPa, 275 MPa, and 12.4% to 320 MPa, 254 MPa, and 6.5% , respectively after T6 heat treatment, together with a continuous declining of tensile strength, tiny variation of yield strength and a continuous variation of elongation. The average length and width size of silicon particles are 10~25 μm and 5~10 μm, respectively, and the morphologies of neonatal and eutectic silicon particles evolve from needle and lamellar structures to spheroidal and rod structures after the T6 heat treatment process. Silicon particles are shown as needle and lamellar mostly when the quenching transfer time exceeds 35 s. The tensile fracture morphology is observed as dimple and intergranular fracture, and the intergranular fracture is increased with the prolonged quenching transfer time. Magnesium and silicon elements are distributed nearby the grain boundaries and the binary and ternary eutectic structures, whereas the aluminium elements are concentrated in the grain and grain boundaries. The length and width size of Mg2Si phase are 0.2~1 μm and 0.02~0.08 μm, respectively, the precipitation amount and size ratio of Mg2Si phase are declined, together with the decreases of strength and ductility of A357 aluminum alloy with the prolonged quenching transfer time.
FAN Zhenzhong
,
ZHENG Weidong
,
ZHANG Xianfeng
,
LI Hong
,
WANG Shaohua
. Influence of Quenching Transfer Time on the Mechanical Properties and Microstructure of A357 Aluminum Alloys[J]. Science & Technology Review, 2014
, 32(32)
: 22
-27
.
DOI: 10.3981/j.issn.1000-7857.2014.32.003
[1] Gall K, Horstemeyer M. Finite element analysis of the stress distributions near damaged Si particle clusters in cast Al-Si alloys[J]. Mechanics of Materials, 2000, 32(4): 277-301.
[2] Fisher J C, Hollomon J H. Precipitation from solid solution[J]. Industrial and Engineering Chemistry, 2002, 44(6): 1324-1327.
[3] Wang Q G, Davidson C J. Solidification and precipitation behavior of Al-Si-Mg casting alloys[J]. Journal of Material Science, 2001, 36(8): 739-750.
[4] Dorward R C. A dynamic quench model for strength predictions in heattreatable aluminum alloys[J]. Journal of Materials Processing Technology, 1997, 66(4): 25-29.
[5] 熊艳才, 刘伯操. 铸造铝合金现状及未来发展[J]. 特种铸造及有色合 金, 1998, 4(1): 1-5. Xiong Yancai, Liu Bocao. Review and prospect of cast aluminum alloy[J]. Special Casting and Nonferrous Alloy, 1998, 4(1): 1-5.
[6] 陈振中, 解传浩, 朱成香. A357铸造铝合金疲劳特性及热处理的影响[J]. 轻金属, 2010(7): 58-61. Chen Zhenzhong, Xie Chuanhao, Zhu Chengxiang. The effects of heat treatment on fatigue properties of A357 casting aluminium alloy[J]. Light Metals, 2010(7): 58-61.
[7] Embury J D, Sargent C M. The effect of quench deformation on the defect structure of quenched metals and alloys[J]. Acta Metallurgica, 1962, 10 (2): 1118-1121.
[8] Myung G K, Sang G K. Thermally induced stress analysis of composite/ aluminum ring specimens at cryogenic temperature[J]. Composities Science and Technology, 2008, 68(4): 1080-1087.
[9] Anjabin N, Karimi A. Physically based material model for evolution of stress-strain behavior of heat treatable aluminum alloys during solution heat treatment[J]. Materials and Design, 2010, 31(1): 433-437.
[10] Francis J A, Delphine C G M. The role of defects in the fracture of an Al-Si-Mg cast alloy[J]. Materials Science and Engineering A, 2005, 407(1-2): 322-329.
[11] Li X L,Hao Q T, Jie W Q. Development of pressure control system in counter gravity casting for large thin- walled A357 aluminum alloy components[J]. Transactions of Nonferrous Metals Society of China, 2008, 18(4): 847-851.
[12] Tan L J, Zabaras N. A thermo-mechanical study of the effects of mold topography on the solidification of aluminum alloys[J]. Materials Science and Engineering A, 2005, 404(1-2): 197-207.
[13] Eskin D G. Recent trends in the science and technology of crystallization of aluminum alloys[J]. Metal Science and Heat Treatment, 2012, 53(9- 10): 408-413.
[14] Wyatt J E, Berry J T, Williams A R. Residual stresses in aluminum castings[J]. Journal of Materials Processing Technology, 2007, 191(1- 3): 170-173.
[15] Carrera E, Rodriguez A, Talamantes J, et al. Measurement of residual stresses in cast aluminium engine blocks[J]. Journal of Materials Processing Technology, 2007, 189(1-3): 206-210.
[16] Jiang L T, Wu G H, Yang W S, et al. Effect of heat treatment on microstructure and dimensional stability of ZL114A aluminum alloy[J]. Transactions of Nonferrous Metals Society of China, 2010, 20(11): 2124-2128.