The curing performance of different 3D printing photosensitive resins varies, which are light cured under the same 3D printer. 2 characteristic parameters, critical exposure and transmission depth, were used to characterize the photosensitivity of photosensitive adhesives, and the mathematical relationship between critical exposure and transmission depth was explored. The measuring methods of critical exposure and penetration depth were studied. The effects of light intensity and resin color on resin curing were measured. Under certain conditions, the penetration depth generally increased with the increase of light intensity,and the critical exposure also increased with the increase of light intensity. Light colors have higher penetration depth than dark colors, and require higher critical exposure. The depth of cure decreases with increasing concentration of photoinitiator. The critical exposure decreases firstly with the increase of photoinitiator concentration, and then tends to be flat.
CHEN Jing
,
YANG Xiaoshuai
,
ZHANG Pengfei
,
ZHANG Aiping
. Studies on the influence factors on Ec and Dp of photocuring 3D printing photosensitive resin[J]. Science & Technology Review, 2024
, 42(4)
: 110
-114
.
DOI: 10.3981/j.issn.1000-7857.2024.04.011
[1] 金养智.光固化材料性能及应用手册[M].第二版.北京:化学工业出版社, 2022:866.
[2] 张颖,朱金华,文庆珍. UV光固化胶黏剂[J].胶体与聚合物, 2008, 26(3):42-43.
[3] 孙芳,黄跃东,熊军.粘接塑料和玻璃用的新型紫外光固化胶粘剂的性能[J].北京化工大学学报, 2006, 33(5):82-85.
[4] Amit B, Bryan H. Additive manufacturing of multi-material structures[J]. Materials Science and Engineering, 2018,129(1):1-16.
[5] Thomas G, Amit B. Additive manufacturing of compositionally gradient metal-ceramic structures:Stainless steel to vanadium carbide[J]. Materials&Design, 2018, 139(1):419-428.
[6] 陈用烈,曾兆华,杨建文.辐射固化材料及其应用[M].北京:北京化学工业出版社, 2003:76.
[7] Jacobs F. Rapid prototyping and manufacturing:fundamentals of stereolithography[M]. Dearborn:SME, 1992.
[8] Jacobs F. Stereolithography and other RP&M technology from rapid prototyping to rapid tooling[M]. Dearborn:SME, 1994.
[9] 刘海涛.光固化三维打印快速成形材料的研究与应用[D].武汉:华中科技大学, 2009.
[10] 俞未一,梅预峰,沈家平.光敏复合树脂的光照时间和距离对其固化作用的实验研究[J].中华口腔医学杂志,1994, 29(6):366-367.
[11] Aravamudhan K, Rakowski D, Fan P L. Variation of depth of cure and intensity with distance using LED curing lights[J]. DentMater, 2006, 22(11):988-994.
[12] 姬亚昆,凌均柴,陈罕,等.卤素和LED光固化灯照射复合树脂的机械强度比较[J].实用口腔医学杂志,2006, 22(2):227-229.